Effect of annealing on the dielectric properties of PZN-PT-BT ceramics
Wang X.1; Chen H.2
2003-05-25
Source PublicationMaterials Science and Engineering B: Solid-State Materials for Advanced Technology
Volume99
Issue1-3
Pages36-40
AbstractThe dielectric behaviors of Pb(ZnNb)O-PbTiO-BaTiO (PZN-PT-BT) ceramics of several compositions have been systematically studied in as-prepared (unannealed) condition as well as after annealing (at 880 °C for 16 h). The general trend seems to indicate that the annealed samples become more ferroelectric-like as opposed to relaxor type in the unannealed state. It also shows a shift of T, the temperature at dielectric maximum, toward higher value after annealing. Both behaviors are composition dependent. X-ray diffraction patterns reveal changes of crystalline structure after annealing, which can be correlated to the accompanied changes in dielectric properties. Those experimental results may be understood using a model of paraelectric BZN nano-phase particles embedded in the PZN-PT-BT matrix. © 2002 Published by Elsevier Science B.V.
KeywordAnnealing Dielectric properties PZN-PT-BT ceramics
DOI10.1016/S0921-5107(02)00445-2
URLView the original
Language英語
Fulltext Access
Citation statistics
Cited Times [WOS]:6   [WOS Record]     [Related Records in WOS]
Document TypeConference paper
CollectionUniversity of Macau
Affiliation1.Xi'an Jiaotong University
2.City University of Hong Kong
Recommended Citation
GB/T 7714
Wang X.,Chen H.. Effect of annealing on the dielectric properties of PZN-PT-BT ceramics[C],2003:36-40.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang X.]'s Articles
[Chen H.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang X.]'s Articles
[Chen H.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang X.]'s Articles
[Chen H.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.