Fiber alignment and property direction dependency of FRC extrudate
Qian X.2; Zhou X.1; Mu B.1; Li Z.1
2003-10-01
Source PublicationCement and Concrete Research
ISSN00088846
Volume33Issue:10Pages:1575-1581
AbstractThis paper studies the phenomenon of fiber alignment during the extrusion process. The fiber alignment is largely dependent on shapes of dies and the compression as well as the shear force generated in the extruder. The fiber alignment orientation, of course, would lead to direction dependency of the tensile properties of fiber-reinforced cement (FRC) extrudates. Such a dependency has been investigated in present study. It is found that when fiber volume ratio is small, say 1% of the glass fiber, the majority of the fiber can be aligned in the extrusion direction. As a result, the tensile strength of the thin plate along the extrusion direction is much higher than that along the transverse direction. When the total fiber volume ratio is increased to 2% or 4%, the fiber volume along the transverse direction is largely increased although the percentage of the fiber aligned along the extrusion direction is still higher. Thus, the tensile strength at a transverse direction can be significantly enhanced. In fact, the tensile strength of the samples along the transverse direction is almost the same as that along the extrusion direction when the fiber volume ratio reaches 2%. Furthermore, the strength of the sample at the extrusion direction does not increase proportionally to the fiber volume ratio. For the comparison purpose, plain sheets without any fibers have been prepared by both casting and extrusion. Mechanical properties of the sheets have also been tested and the test results show that extrusion process and fiber addition do have effects on enhancing the tensile properties. Polymer coating on the surface of the samples has also been used to improve the tensile properties of the extrudates with low fiber volume ratio, which shows some promising results. © 2003 Elsevier Ltd. All rights reserved.
KeywordCement Extrusion technique Fiber distribution Fiber-reinforced composite Tension
DOI10.1016/S0008-8846(03)00108-X
URLView the original
Language英語
全文获取链接
引用统计
被引频次[WOS]:30   [WOS记录]     [WOS相关记录]
Document TypeJournal article
专题University of Macau
Affiliation1.Hong Kong University of Science and Technology
2.Zhejiang University
推荐引用方式
GB/T 7714
Qian X.,Zhou X.,Mu B.,et al. Fiber alignment and property direction dependency of FRC extrudate[J]. Cement and Concrete Research,2003,33(10):1575-1581.
APA Qian X.,Zhou X.,Mu B.,&Li Z..(2003).Fiber alignment and property direction dependency of FRC extrudate.Cement and Concrete Research,33(10),1575-1581.
MLA Qian X.,et al."Fiber alignment and property direction dependency of FRC extrudate".Cement and Concrete Research 33.10(2003):1575-1581.
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
Google Scholar
中相似的文章 Google Scholar
[Qian X.]的文章
[Zhou X.]的文章
[Mu B.]的文章
Baidu academic
中相似的文章 Baidu academic
[Qian X.]的文章
[Zhou X.]的文章
[Mu B.]的文章
Bing Scholar
中相似的文章 Bing Scholar
[Qian X.]的文章
[Zhou X.]的文章
[Mu B.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。