Influences of a new admixture MX on concrete durability
Ma B.; Dong R.; Zhu H.; Zhang L.; Zhong K.; He X.; Li Z.
2005-03-01
Source PublicationJournal Wuhan University of Technology, Materials Science Edition
ISSN10002413
Volume20Issue:1Pages:117-120
AbstractThe performance of concrete with a new admixture MX was studied by using the freeze-thaw cycle, permeability and chemical attack test. The experimental results show that MX improves the durability of concrete. Within the optimum proportion ranges from 0.1% to 1%, the compressive strength of concrete after freeze-thaw is increased by 20%-50%, and Young's modulus can be increased by 3.76-5.64 times. The strength and weight loss of concrete with 0.4% MX are respectively decreased by 28% and 60% after hydrochloric acid attack. The strength and weight loss of concrete with 0.4% MX are decreased by 5%-20% after sulfuric acid and sodium sulfate attack. The permeability of concrete with 1% MX at 28 days can be decreased by more than 30%. The investigation of the negative temperature property of MX and analysis on concrete composition and microstructure by MIP reveal that the heat conduction is resisted and the freezing procedure of solution in concrete pore is retarded due to the adding of MX. Moreover, the pore structure of concrete with MX is improved, thus improving the durability. Based on this study, a resistance model of MX to block the heat and mass transference was proposed, and the mechanism of durability improvement of concrete with MX was explained.
KeywordMX durability admixture Negative temperature property Ratio of strength loss
URLView the original
Language英語
Fulltext Access
Document TypeJournal article
CollectionUniversity of Macau
AffiliationWuhan University of Technology
Recommended Citation
GB/T 7714
Ma B.,Dong R.,Zhu H.,et al. Influences of a new admixture MX on concrete durability[J]. Journal Wuhan University of Technology, Materials Science Edition,2005,20(1):117-120.
APA Ma B..,Dong R..,Zhu H..,Zhang L..,Zhong K..,...&Li Z..(2005).Influences of a new admixture MX on concrete durability.Journal Wuhan University of Technology, Materials Science Edition,20(1),117-120.
MLA Ma B.,et al."Influences of a new admixture MX on concrete durability".Journal Wuhan University of Technology, Materials Science Edition 20.1(2005):117-120.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Ma B.]'s Articles
[Dong R.]'s Articles
[Zhu H.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Ma B.]'s Articles
[Dong R.]'s Articles
[Zhu H.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Ma B.]'s Articles
[Dong R.]'s Articles
[Zhu H.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.