Room-temperature electrosynthesized ZnO thin film with strong (0 0 2) orientation and its optical properties
Mei Y.F.1; Siu G.G.1; Fu R.K.Y.1; Chu P.K.1; Li Z.M.2; Tang Z.K.2
2006-02-15
Source PublicationApplied Surface Science
ISSN01694332
Volume252Issue:8Pages:2973-2977
AbstractZnO thin film with strong orientation (0 0 2) and smooth surface morphology was electrosynthesized on ITO-coated glass substrate at room temperature under pulsed voltage. Photoluminescence (PL) shows two obvious peaks: violet band and strong green band. The former is due to the free-excitonic transition and the latter is believed to arise from the single ionized oxygen vacancy (V ). Raman scattering reveals that the 580 cm mode and the shoulder peak mode at 550 cm originate from the N-related local vibration mode (LVM) and E (LO) mode, respectively. © 2005 Elsevier B.V. All rights reserved.
KeywordElectrodeposition II-VI semiconductors Infrared and Raman spectra Photoluminescence
DOI10.1016/j.apsusc.2005.05.004
URLView the original
Language英語
Fulltext Access
Citation statistics
Cited Times [WOS]:25   [WOS Record]     [Related Records in WOS]
Document TypeJournal article
CollectionUniversity of Macau
Affiliation1.City University of Hong Kong
2.Hong Kong University of Science and Technology
Recommended Citation
GB/T 7714
Mei Y.F.,Siu G.G.,Fu R.K.Y.,et al. Room-temperature electrosynthesized ZnO thin film with strong (0 0 2) orientation and its optical properties[J]. Applied Surface Science,2006,252(8):2973-2977.
APA Mei Y.F.,Siu G.G.,Fu R.K.Y.,Chu P.K.,Li Z.M.,&Tang Z.K..(2006).Room-temperature electrosynthesized ZnO thin film with strong (0 0 2) orientation and its optical properties.Applied Surface Science,252(8),2973-2977.
MLA Mei Y.F.,et al."Room-temperature electrosynthesized ZnO thin film with strong (0 0 2) orientation and its optical properties".Applied Surface Science 252.8(2006):2973-2977.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Mei Y.F.]'s Articles
[Siu G.G.]'s Articles
[Fu R.K.Y.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Mei Y.F.]'s Articles
[Siu G.G.]'s Articles
[Fu R.K.Y.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Mei Y.F.]'s Articles
[Siu G.G.]'s Articles
[Fu R.K.Y.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.