Fabrication of nano-structured HA/CNT coatings on Ti6A14V by electrophoretic deposition for biomedical applications
Zhang B.2; Kwok C.T.2; Cheng F.T.1; Man H.C.1
2010-05-05
Source PublicationINEC 2010 - 2010 3rd International Nanoelectronics Conference, Proceedings
Pages813-814
AbstractIn order to improve the bone bioactivity and osteointegration of metallic implants, hydroxyapatite (HA) is often coated on their surface so that a real bond with the surrounding bone tissue can be formed. In the present study, cathodic electrophoretic deposition (EPD) has been attempted for depositing nanostructured HA coatings on titanium alloy Ti6A14V followed by sintering at 800 °C. Nano-sized HA powder was used in the EPD process to produce dense coatings. Moreover, multi-walled carbon nanotubes (CNTs) were also used to reinforce the HA coating for enhancing its mechanical strength. The surface morphology, compositions and microstructure of the monolithic coating of HA and composite coatings of HA with different CNT contents (5 to 20%) on Ti6A14V were investigated by scanning electron microscopy, energy-dispersive X-ray spectroscopy and X-ray diffractometry, respectively. Electrochemical corrosion behavior of the various coatings in Hanks' solution at 37 °C was investigated by means of open-circuit potential measurement and cyclic potentiodynamic polarization tests. Surface hardness, adhesion strength and bone bioactivity of the coatings were also studied. The HA and HA/CNT coated Ti6A14V had a thickness of about 10 μm without cracks, with corrosion resistance higher than that of the substrate and adhesion strength higher than that of plasma sprayed HA coating. The properties of the composite coatings were optimized by varying the CNT contents. The enhanced properties could be attributed to the use of nano-sized HA particles and CNTs. Compared with the monolithic HA coating, the CNT-reinforced HA coating markedly increased the coating hardness without deteriorating the corrosion resistance or adhesion strength. ©2010 IEEE.
DOI10.1109/INEC.2010.5425191
URLView the original
Language英語
全文获取链接
引用统计
Document TypeConference paper
专题DEPARTMENT OF ELECTROMECHANICAL ENGINEERING
Affiliation1.Hong Kong Polytechnic University
2.Universidade de Macau
推荐引用方式
GB/T 7714
Zhang B.,Kwok C.T.,Cheng F.T.,et al. Fabrication of nano-structured HA/CNT coatings on Ti6A14V by electrophoretic deposition for biomedical applications[C],2010:813-814.
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
Google Scholar
中相似的文章 Google Scholar
[Zhang B.]的文章
[Kwok C.T.]的文章
[Cheng F.T.]的文章
Baidu academic
中相似的文章 Baidu academic
[Zhang B.]的文章
[Kwok C.T.]的文章
[Cheng F.T.]的文章
Bing Scholar
中相似的文章 Bing Scholar
[Zhang B.]的文章
[Kwok C.T.]的文章
[Cheng F.T.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。